Rajpurohit, R S and Jena, P S M and Mahato, B and Sahu, J K (2020) Strain partitioning between matrix and precipitates during fatigue deformation of 2.25Cr-Mo steel. Material Science and Technology (IF-1.835).
Full text not available from this repository. (Request a copy)Abstract
The influence of stress rate on load/strain partitioning between different phases of a micro-alloyed 2.25Cr-Mo steel during stress-controlled fatigue deformation at room temperature (RT) was studied by conducting asymmetrical ratcheting fatigue tests employing values of 50-450 MPa/s. Fatigue life (N-f) significantly reduced for tests conducted by employing = 50 MPa/s compared to 450 MPa/s, i.e. N-f = 510 and 24,983 cycles respectively. From TEM studies, it is confirmed that due to load/strain partitioning stacking faults (SFs)/micro-twin formed in M23C6 carbides during high fatigue deformation, whereas dislocation cells are formed in low fatigue deformation. A plausible explanation to account for different cycle life with change in of fatigue deformation is offered.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | Cyclic strain; defects; fatigue life; M23C6 carbide; stacking faults; microstructure; micro-twin;carbides |
| Subjects: | Metallurgy > Steel Metallurgy |
| Divisions: | Material Science and Technology |
| Depositing User: | Users 5 not found. |
| Date Deposited: | 11 Jun 2020 05:07 |
| Last Modified: | 17 Nov 2020 09:38 |
| URI: | http://eprints.nmlindia.org/id/eprint/8151 |
Actions (login required)
- View Item