Soft magnetic properties of Fe-based bulk metallic glass system containing niobium and copper

Anjaneyulu, Ch and Murty, B S (2017) Soft magnetic properties of Fe-based bulk metallic glass system containing niobium and copper. Journal of Metallurgy and Materials Science, 59(3) . pp. 103-110.

[img]PDF
Restricted to NML users only. Others may use ->

514Kb

Abstract

investigated with SEM, XRD technique. BMG rods were then prepared by conventional suction casting through copper mould. The XRD pattern of glassy rods exhibit few crystalline phases in all the alloy samples. The suppression of crystalline peaks to a reasonable extent is evident from respective XRD pattern of amorphous rods. Good extent of GFA was achieved with three alloy samples. However the GFA of Fe_1 sample is better than remaining two, but its saturation magnetisation is very poor. Fe_3 sample give better saturation magnetisation Is and its GFA is moderate. Good GFA of Fe_1 sample correlates with higher squareness ratio of the same. The Percentage relative The alloy ingots with three different nominal compositions were prepared and change of density and squareness ratio have same trend of variations. However these three samples exhibit very low squareness ratio. The magnetic properties of Fe_4 sample were intermediate between Fe_1 and Fe_3 samples. Hysteresis loss is found to be least for Fe_1 sample. Hence low Hysteresis loss and good GFA were correlated during this study. It was also observed that saturation magnetisation is high for the sample containing 3mol% of Nb.

Item Type:Article
Official URL/DOI:http://eprints.nmlindia.org/7851
Uncontrolled Keywords:GFA, Soft Magnetic Properties, Hysteresis Loss, Squareness ratio and Percentage relative change of density.
Divisions:Material Science and Technology
ID Code:7851
Deposited By:Dr. A K Sahu
Deposited On:07 Aug 2018 15:01
Last Modified:07 Aug 2018 16:33
Related URLs:

Repository Staff Only: item control page