Mandal, D and Ghosh, M and Pal, J and De, P K and Ghosh Chowdhury, S and Das, S K and Das, Goutam and Ghosh, Sukomal (2006) Influence of Austempering Temperature on Microstructure and Mechanical Properties of Cast Fe-Si-Mn-VSteel. In: 60 Annual Technical Meeting, November, 14-16, 2006, NML, Jamshedpur.

[img]PDF
Restricted to NML users only. Others may use ->

646Kb

Abstract

The present investigation was carried out to examine the influence of austempering temperature on the micro-structure and mechanical properties of a low carbon, high silicon (C-0.13%, Si-1.2%, Mn-1%, V-0.08%) cast steels. The Induction melted casting block was homogenized at 1000°C for 6 hrs. The samples for microstructure and the tens-ile specimens were prepared from the cast steel block according to ASTM standards and were imparted three diff-erent austempering heat treatments to produce different microstructure. The samples are austenitisation at 900°C for 30 minute and then rapidly quenched to a salt bath maintained at temperature 350/400/450°C for 10 minute and then finally air cooled. The microstructure were observed under optical and TEM microscopy. show that UTS decreases but % El increases with increasing apstempering tempe-rature. The 400°C austempering temperature exhibited the best combination of UTS and %EI at room temperature (UTS-663 MPa, EL-26%) with revealing microstructure of bainite and retained austenite.

Item Type:Conference or Workshop Item (Paper)
Official URL/DOI:http://eprints.nmlindia.org/5740
Uncontrolled Keywords:Microstructure; bainite; austenite; mechanical properties
Divisions:Material Science and Technology
ID Code:5757
Deposited By:Sahu A K
Deposited On:10 Jul 2012 13:13
Last Modified:01 Dec 2012 11:26
Related URLs:

Repository Staff Only: item control page