Ghosh, M and Kar, Abhijit and Kumar, K and Kailas, S V (2012) Structural characterisation of reaction zone for friction stir welded aluminium–stainless steel joint. Materials Technology, 27 (2). pp. 169-172.
|PDF - Published Version |
Restricted to NML users only. Others may use ->
In the present investigation, commercially pure Al has been joined with 304 stainless steel (SS) by friction stir welding. The assembly finds widespread application in the field of cryogenics, nuclear, structural industries and domestic appliances. Microstructural characterisation was carried out using scanning and transmission electron microscopes. It has been found that diffusion of Fe, Cr and Ni is substantial within Al; however, diffusion of Al within 304SS is limited. Owing to interdiffusion of chemical species across the bondline, discrete islands of Fe3Al intermetallic form within the reaction zone. The rubbing action of tool over the butting edge of 304SS removed fine particles from 304SS, which were embedded in the stirring zone of Al matrix. Subsequently, austenite underwent phase transformation to ferrite due to large strain within this grain. Fracture path mainly moves through stirring zone of Al alloy under tensile loading; however, in some places, presence of Fe3Al compound has been also found.
|Uncontrolled Keywords:||Friction stir welding, Aluminium, Stainless steel, Intermetallics, Electron microscopy|
|Divisions:||Material Science and Technology|
|Deposited By:||Dr Mainak Ghosh|
|Deposited On:||18 May 2012 14:28|
|Last Modified:||18 May 2012 14:28|
Repository Staff Only: item control page