Effect of nickel on sintering of self-propagating high-temperature synthesis produced titanium carbide

Mishra, Suman K and Das, Swapan K and Ray, Ajoy K and Ramachandrarao, P (1999) Effect of nickel on sintering of self-propagating high-temperature synthesis produced titanium carbide. Journal of Materials Research, 14 (9). pp. 3594-3598.

Full text not available from this repository.

Abstract

A detailed study of the sintering behavior of titanium carbide (TiC) powder synthesized by the self-propagating high-temperature synthesis (SHS) route was carried out with varying percentages of nickel. With an increase in the nickel content, porosity was found to increase along with Ni2.67Ti1.33 secondary phase at grain boundary. A 90-92% dense sintered body of TiC was produced from SHS-produced powder at 1800 degrees C with 10 wt% nickel.

Item Type:Article
Official URL/DOI:http://www.nmlindia.org
Uncontrolled Keywords:Combustion synthesis; synthesis shs
Divisions:Material Science and Technology
ID Code:1142
Deposited By:Sahu A K
Deposited On:22 Jun 2010 17:54
Last Modified:25 Jan 2012 10:15
Related URLs:

Repository Staff Only: item control page