Shimoda, Hideo and Onodera, S (1953) A Contribution to the Service Failure of Large Chilled Iron Rolls due to Fatigue. In: Symposium on Industrial Failure of Engineering Metals & Alloys, Feb. 5-7, 1953, NML, Jamshedpur.
![[thumbnail of 17-30.PDF]](http://eprints.nmlindia.org/style/images/fileicons/application_pdf.png "17-30.PDF")
PDF
17-30.PDF
Download (3MB)
Abstract
A case of service rupture of chilled iron roll due to fatigue is presented with condition of rupture, invest-igation of the cause, and remedial result through remo-delling.
As a result of this, it is suggested that service strength of chilled iron rolls should be considered
through fatigue, and that standard size is not necessar-ily of sufficient strength from this point of view ; a remark for the prevention of service failures in existent mills, and to which reference is desired to make in bui-lding new mills
| Item Type: | Conference or Workshop Item (Paper) |
|---|---|
| Uncontrolled Keywords: | Iron rolls, Fabrication, Bending stress |
| Subjects: | Metallurgy |
| Divisions: | Metal Extraction and Forming |
| Depositing User: | Users 5 not found. |
| Date Deposited: | 15 Jul 2011 06:07 |
| Last Modified: | 26 Dec 2011 08:52 |
| URI: | http://eprints.nmlindia.org/id/eprint/3364 |
Actions (login required)
- View Item