Das, Swapan K and Narasaiah, N and Sivaprasad, S and Chatterjee, S and Tarafder, S (2007) Effect of aging on fatigue crack growth behaviour of Cu bearing HSLA-100 steel. Materials Science and Technology, 23 (2). pp. 177-182.
![[thumbnail of Swapan-MST-2007.pdf]](http://eprints.nmlindia.org/style/images/fileicons/application_pdf.png "Swapan-MST-2007.pdf")
PDF
Swapan-MST-2007.pdf
Restricted to NML users only. Others may use ->
Download (410kB) | Request a copy
Abstract
The effect of aging on fatigue crack growth rate (FCGR) of Cu bearing HSLA-100 steel has been studied. The steel was solution treated, water quenched and aged at various temperatures in the range of 350-700°C. The fatigue crack growth resistance of the steel decreased for the initial stages of aging from 350-500°C. Further aging up to 650°C resulted in an improvement in the crack growth resistance. Beyond 650°C, once again an inferior crack growth resistance was observed. This nature of variation of FCGR behaviour was similar to the trend portrayed by the strength properties with aging treatment. The results are related to the changes in the microstructural constituents owing to the aging treatment.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | Aging; Copper Precipitation; HSLA-100 steel; FCGR; Microstructure |
| Subjects: | Metallurgy |
| Divisions: | Material Science and Technology |
| Depositing User: | Users 6 not found. |
| Date Deposited: | 28 Jul 2010 10:18 |
| Last Modified: | 02 Sep 2026 12:53 |
| URI: | http://eprints.nmlindia.org/id/eprint/1333 |
Actions (login required)
- View Item