The Effect of Residual Stress on Fatigue crack growth rate in AISI 304LN Stainless Steel

Prakash, Amit and Bar, H N and Sivaprasad, S and Tarafder, S and Dwivedi, J P (2017) The Effect of Residual Stress on Fatigue crack growth rate in AISI 304LN Stainless Steel. Materials Today: Proceedings, 4(2) . pp. 677-686.

[img]PDF
Restricted to NML users only. Others may use ->

2211Kb

Abstract

Fatigue crack growth rate (FCGR) was studied in SMAT- exposed AISI 304LN stainless steel. Compact Tension (CT) specimens were taken for this study. Specimens were exposed to SMAT at various exposure timefor generating varying compressive residual stresses and FCGR study was done on those specimens at R=-1. It was seen that exposure to SMAT, produced micro-cracks within the material that increased the FCGR of the material with increased exposure time.

Item Type:Article
Official URL/DOI:DOI: 10.1016/j.conbuildmat.2017.04.174
Uncontrolled Keywords:Fatigue crack growth rate (FCGR)Surface mechanical attrition treatment (SMAT)Residual stressAISI 304LN
Divisions:Material Science and Technology
ID Code:7615
Deposited By:Sahu A K
Deposited On:18 Aug 2017 17:43
Last Modified:02 Nov 2017 13:26
Related URLs:

Repository Staff Only: item control page