Prashanth, K G and Shahabi, H S and Attar, H and Srivastava, V C and Eckert, J and Scudino, S and Uhlenwinkel, V and Ellendt, N (2015) Production of high strength Al85Nd8Ni5Co2 alloy by selective laser melting. Additive Manufacturing, 6 . pp. 1-5.
Restricted to NML users only. Others may use ->
Bulk high strength and thermally stable Al 85 Nd 8 Ni 5 Co 2 samples have been prepared by selective laser melting (SLM). The alloy shows a composite-like microstructure consisting of submicron-sized stable intermetallic phases dispersed in an Al matrix, which leads to high compressive strength (1–0.5 GPa) at elevated temperatures (303–573 K). These results indicate that SLM is an effective alternative to conventional routes for producing dense, thermally stable and near net shaped components from high strength Al-based alloys.
|Uncontrolled Keywords:||Additive manufacturing; Aluminum alloys; Intermetallic compounds; Compression test|
|Divisions:||Metal Extraction and Forming|
|Deposited By:||Dr. V.C. Srivastava|
|Deposited On:||03 Feb 2015 16:35|
|Last Modified:||03 Feb 2015 16:35|
Repository Staff Only: item control page