Balusamy, T and Satendra, Kumar and Sankara Narayanan, T S N (2010) Effect of surface nanocrystallization on the corrosion behaviour of AISI 409 stainless steel. Corrosion Science, 52 . pp. 3826-3834.
![[img]](/style/images/fileicons/application_pdf.png) | PDF 2161Kb |
Abstract
The influence of surface mechanical attrition treatment (SMAT) on the corrosion behaviour of AISI 409 grade stainless steel in 0.6 M NaCl was studied. SMAT using 2 mm £ 316L stainless steel (SS) balls for 15, 30 and 45 min and 5 mm £ balls for 15 min offers a better corrosion protective ability. In contrast, treatment using 5 mm £ balls for 30 and 45 min and by using 8 mm £ balls for 15, 30 and 45 min,induces microstrain and defect density that results in a decrease in corrosion resistance.
| Item Type: | Article |
|---|---|
| Official URL/DOI: | doi:10.1016/j.corsci.2010.07.004 |
| Uncontrolled Keywords: | Steel; EIS; Polarization; XRD; Passivity |
| Divisions: | NML Chennai > Chemistry |
| ID Code: | 1530 |
| Deposited By: | Dr. TSN Sankara Narayanan |
| Deposited On: | 06 Sep 2010 16:59 |
| Last Modified: | 13 Dec 2011 16:11 |
| Related URLs: |
Repository Staff Only: item control page