Mandal, D and Ghosh, M and Pal, J and De, P K and Ghosh Chowdhury, S and Das, S K and Das, Goutam and Ghosh, S (2009) Effect of austempering treatment on microstructure and mechanical properties of high-Si steel. Journal of Materials Science, 44 (4). pp. 1069-1075.
Restricted to NML users only. Others may use ->
In the present investigation, the influence of austempering treatment on the microstructure and mechanical properties of silicon alloyed cast steel has been evaluated. The experimental results show that an ausferrite structure consisting of bainitic ferrite and retained austenite can be obtained by austempering the silicon alloyed cast steel at different austempering temperature. TEM observation and X-ray analysis confirmed the presence of retained austenite in the microstructure after austempering at 400 °C. The austempered steel has higher strength and ductility compared to as-cast steel. With increasing austempering temperature, the hardness and strength decreased but the percentage of elongation increased. A good combination of strength and ductility has been obtained at an austempering temperature of 400 °C.
|Uncontrolled Keywords:||Austenite;Ductility;Mechanical properties; Microcrystalline silicon; Steel metallurgy; Wear resistance;|
|Divisions:||Metal Extraction and Forming|
|Deposited By:||Madhan M|
|Deposited On:||20 Sep 2009 01:58|
|Last Modified:||11 Jan 2012 17:47|
Repository Staff Only: item control page