Pathak, L C and Mishra, Suman K and Bhattacharyya, D and Chopra, K L (1999) Sintering characteristics of Y-Ba-Cu-oxide-Ag-x superconductors. Journal of Materials Research, 14 (11). pp. 4148-4156.
Full text not available from this repository.
The sintering characteristics of Y-Ba-Cu-oxide (YBCO)-Ag-x (x = 0 to 1.2) using thermomechanical analyzer were systematically investigated to understand the sintering mechanism of the metal superconductor composites. The addition of ag was observed to lower the sintering temperatures, and the apparent densities of the sintered compacts increased with x from 0 to 0.6. A further increase of x above 0.6 decreased the apparent densities of the sintered compacts. The presence of Ag globules in the YBCO-Ag compacts was observed by scanning electron microscopy and energy dispersive x-ray spectroscopy. The apparent activation energies for sintering of the powder compacts were estimated and observed to vary between 900 to 2000 kJ/mol. The formation of AgOx by absorbing oxygen from YBCO and sintering atmosphere possibly controls the sintering and superconducting behavior, incorporation of Ag into the matrix modifies the weak-link characteristics from superconductor-insulator-normal- superconductor (S-I-N-S) to superconductor-normal-superconductor (S-NS) type.
|Uncontrolled Keywords:||Y-Ba-Cu-oxide-Ag-x superconductors|
|Divisions:||Material Science and Technology|
|Deposited By:||Sahu A K|
|Deposited On:||22 Jun 2010 17:51|
|Last Modified:||07 Feb 2012 14:56|
Repository Staff Only: item control page