Mishra, Suman K and Bhople, A and Paswan, S (2014) Microstructure, hardness, toughness and oxidation resistance of Al2O3-ZrB2 composite with different Ti percentages prepared by in-situ SHS dynamic compaction. International Journal of Refractory Metals and Hard Materials, 43 (IF-1.764). pp. 7-12.
![[thumbnail of S.K._Mishra,IJRMHM_2014_PP-7-12.pdf]](http://eprints.nmlindia.org/style/images/fileicons/application_pdf.png "S.K._Mishra,IJRMHM_2014_PP-7-12.pdf")
PDF
S.K._Mishra,IJRMHM_2014_PP-7-12.pdf
Restricted to NML users only. Others may use ->
Download (2MB) | Request a copy
Abstract
Effect on microstructure, hardness, modulus, fracture toughness and oxidation behaviour of Al2O3-ZrB2 composite with different percentages of Titanium as diluents during the SHS reaction has been studied. It was observed that Ti addition leads to formation of different phases such as TiB2, ZrO2,TiB besides ZrB2 and Al2O3. The hardness and modulus were found to be around 21 GPa and 350 GPa, respectively for 10 wt.% Ti addition in dynamic depth indentation. Oxidation study of the sample having 25 wt.% Titanium showed no significant change in phase and mechanical properties after 700 degrees C oxidation. The toughness of 20 wt.% Ti sample showed highest fracture toughness. (C) 2013 Elsevier Ltd. All rights reserved
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | Alumina-boride; Composite; Toughness; SHS; Oxidation; Hardness |
| Subjects: | Materials Science |
| Divisions: | Material Science and Technology |
| Depositing User: | Users 5 not found. |
| Date Deposited: | 05 Jun 2014 06:32 |
| Last Modified: | 04 May 2016 08:56 |
| URI: | http://eprints.nmlindia.org/id/eprint/6943 |
Actions (login required)
- View Item