Mahato, P and Mishra, Suman K (2019) A prolonged exposure of Ti-Si-B-C nanocomposite coating in 3.5 wt% NaCl solution: Electrochemical and morphological analysis. Surface and Coatings Technology, 375. pp. 477-488.
Full text not available from this repository. (Request a copy)Abstract
The electrochemical behaviour of magnetron sputtered Ti-Si-B-C nanocomposite coating on SS 304 substrate has been examined using potentiodynamic polarization and electrochemical impedance spectroscopy after long time immersion (1, 20, 40, 70 days) in 3.5 wt% NaCl solution. The surface morphology, elemental composition and surface topography of coated and uncoated surfaces have been analyzed using FESEM, EDX spectroscopy and AFM, respectively. The XRD study revealed the presence of TiB2 and TiSi2 phases in the film which were exposed to 70 days immersion test. It implies that the grains of TiB2 and TiSi2 have grown on the Ti-Si-B-C coating. The results obtained from the electrochemical measurements of sputtered coatings showed the increase of corrosion inhibition capability for Ti-Si-B-C coating compared to SS 304 as the immersion time increases in simulated marine environment.
Graphical abstract
Magnetron sputtered Ti-Si-B-C nanocomposite film on SS 304 as anticorrosive coating and its electrochemical analysis.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | magnetron;potentiodynamic polarization;FESEM, EDX spectroscopy;AFM,Ti-Si-B-C nanocomposite |
| Subjects: | Materials Science > Nano Composites |
| Divisions: | Material Science and Technology |
| Depositing User: | Users 5 not found. |
| Date Deposited: | 30 Sep 2019 05:11 |
| Last Modified: | 30 Sep 2019 05:11 |
| URI: | http://eprints.nmlindia.org/id/eprint/7986 |
Actions (login required)
- View Item