Balusamy, T and Sankara Narayanan, T S N and Ravichandran, K and Park, Song and Lee, Min Ho (2013) Influence of surface mechanical attrition treatment (SMAT) on the corrosion behaviour of AISI 304 stainless steel. Corrosion Science, 74 (IF-3.615). pp. 332-344.
![[thumbnail of balusamy3-2013.pdf]](http://eprints.nmlindia.org/style/images/fileicons/application_pdf.png "balusamy3-2013.pdf")
PDF
balusamy3-2013.pdf
Restricted to NML users only. Others may use ->
Download (5MB) | Request a copy
Abstract
The influence of surface mechanical attrition treatment (SMAT) on the corrosion behaviour of AISI 304 stainless steel in 0.6 M NaCl was studied. SMAT of 304 SS induced plastic deformation, enabled formation of mechanical twins and strain induced ά-martensite phase, increased the surface roughness and imparted compressive residual stress. SMAT caused a deleterious influence on the corrosion resistance of 304 SS in 0.6 M NaCl. Double log plots of current–time transients at 25 mV(SCE) indicate formation of defective passive film on SMATed 304 SS. Increase in surface roughness, strain induced martensite and dislocations nullify the beneficial influence of surface nanocrystallization
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | A. Stainless steel; B. Polarization; B. Potentiostatic; B. EIS; C. Passive films; C. Pitting corrosion |
| Subjects: | Mechanical Engineering |
| Divisions: | NML Chennai |
| Depositing User: | Users 5 not found. |
| Date Deposited: | 11 Sep 2013 11:58 |
| Last Modified: | 04 Apr 2014 10:21 |
| URI: | http://eprints.nmlindia.org/id/eprint/6686 |
Actions (login required)
- View Item