Effect of rare-earth Elements on Nanophase Evolution, Crystallization Behaviour and Mechanical Properties in Al-Ni-R (R = La/Mischmetal) Amorphous Alloys

The crystallization behaviour and evolution of nanoparticles in amorphous Al-Ni-Mischmetal (Mm) and Al-Ni-La alloys during heat treatment have been studied. Rapidly solidified ribbons were obtained by induction melting and ejecting the melt onto a rotating Cu wheel in an Ar atmosphere. The crystallization behaviour of the melt-spun ribbons was investigated using differential scanning calorimetry and X-ray diffractometry (XRD). XRD studies confirmed that all the ribbons were fully amorphous. Al-Ni-Mm systems showed a three-stage crystallization process whereas Al-Ni-La system, in general, showed a two-stage crystallization process on annealing. Crystallization kinetics was analysed by Kissinger and Johnson-Mehl-Avrami approaches. In Al-Ni-La alloys, the crystallization pathways depend on the La concentration. Microhardness of all the ribbons was examined at different temperatures and correlated with the corresponding evolution of phases.