Kumari, Seema and Chattoraj, I and Pal, S K and Mitra, A (2006) Study of Giant Magneto-Impedance Behavior in Co–Fe Based Amorphous/Nanocrystalline Materials. Materials and Manufacturing Processes, 21. pp. 683-686.
![[thumbnail of 20-S_Kumari_(2006).pdf]](http://eprints.nmlindia.org/style/images/fileicons/application_pdf.png "20-S_Kumari_(2006).pdf")
PDF
20-S_Kumari_(2006).pdf - Published Version
Restricted to NML users only. Others may use ->
Download (461kB) | Request a copy
Abstract
Giant magneto-impedance (GMI) behavior have been studied in melt spun Co71−XFeXCr7Si8B14 (X = 0 2 32 4 6 8, and 12 at%) alloys. The addition of Fe in the system changed the saturation magnetostriction constant from negative to positive values. The GMI property was measured with a driving current of 5mA and 4MHz frequency using a spectrum analyzer. The GMI ratio increased with the increase of the applied dc field and became maximum at a field Hk known as the anisotropy field of the materials. The maximum of GMI ratio (GMImax) depended on the Fe content and was maximum (12%) for Fe = 4 at% for the alloys in the as-melt spun state. Substantial increase of GMImax to 66% for Fe = 4 at%
was observed after annealing the sample at 673 K.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | Amorphous ribbons; Giant magnetoimpedance; Magnetostriction |
| Subjects: | Materials Science |
| Divisions: | Corrosion and Surface Engineering |
| Depositing User: | Users 6 not found. |
| Date Deposited: | 01 Sep 2010 10:40 |
| Last Modified: | 02 Sep 2026 13:57 |
| URI: | http://eprints.nmlindia.org/id/eprint/1517 |
Actions (login required)
- View Item