Performance and mechanism of action of self-priming organic coating on oxide covered steel surface

Singh, D D N and Bhattacharya, D (2010) Performance and mechanism of action of self-priming organic coating on oxide covered steel surface. Progress in Organic Coatings, 67 (2). pp. 129-136.

Full text not available from this repository.


Performance and mechanism of action of a self-priming organic coating formulated by incorporating a linear vinyl terpolymer with appended hydroxyl, acetyl and formal groups, a short oil alkyd resin, alkoxy amino resin cross linkers, extenders and pigments, applied on abraded rust free and rust covered steel surfaces are discussed. During the period of test (4400 h, exposed in 3.5% sodium chloride) it was observed that the coating maintained polarization resistance in the range of giga ohms. Under all conditions of tests, it was noted that the coating applied on steel surface covered with rust performed superior than applied on abraded rust free surface. The studies reveal that phosphoric acid added in coating during its preparation reacts with poly vinyl alcohol to form ester. The ester is diffused to rust present on steel substrate during exposure of coated surface in aqueous environment and transforms originally present mixed phases of rust into a stable phase of maghemite. This transformed layer of rust adheres strongly with O–P–O bond available in binder of coating and forms a passive film resulting in its improved performance

Item Type:Article
Official URL/DOI:
Uncontrolled Keywords:Self-priming organic coating; Terpolymer; Phosphate ester; Raman spectroscopy; Electrochemical impedance; Rusted steel surface
Divisions:Corrosion and Surface Engineering
ID Code:488
Deposited By:Sahu A K
Deposited On:13 May 2010 11:36
Last Modified:09 Feb 2012 12:29
Related URLs:

Repository Staff Only: item control page